Foldable backplate film and method for manufacturing foldable backplate film

ABSTRACT

Provided are a foldable back plate film and a method of manufacturing the same.

This application is a 35 U.S.C. 371 National Phase Entry Application from PCT/KR2019/015514 filed on Nov. 14, 2019, designating the United States, which claims priority to and the benefits of Korean Patent Application No. 10-2018-0145352, filed with the Korean Intellectual Property Office on Nov. 22, 2018, the entire contents of which are incorporated herein by reference.

TECHNICAL FIELD

The present application relates to a foldable back plate film and a method of manufacturing the same.

BACKGROUND OF THE INVENTION

Recently, with the development of display-related technology, display devices that can be deformed during use, such as folding, rolling up into a roll, or stretching like a rubber band, are being researched and developed. Since these displays can be deformed in various forms, they can satisfy both the demand for enlargement of the displays during use and the demand for downsizing of the displays for portability.

Deformable display devices may be deformed in a predetermined form, or may be deformed in various forms as desired by a user or in accordance with the requirements of the situation in which the display devices are used. Therefore, it is necessary to recognize the modified forms of displays and to control display devices in response to the recognized forms.

Meanwhile, since deformable display devices have a problem in which the respective components of the display devices are damaged due to the deformation, the respective components of the display devices should satisfy folding reliability and stability.

In particular, in recent years, flexible substrates are mainly used for thinning displays. Display panels using flexible substrates are excessively thin, and thus back plates capable of supporting the display panels are attached to the bottom of the flexible substrates.

Since foldable displays involve folding and unfolding operations, it is essential to attach a support, serving as a guide for operation, to the bottom of the substrates of the foldable displays. In the case of conventional back plates for displays, the cross-section of the substrate is coated with an adhesive and thus an additional process of forming a tackifier or an adhesive agent is needed in order to attach the support, serving as a guide, to the bottom thereof.

Thus, there is the need for research on foldable back plates that are used for foldable displays and enable supports to be attached to back plates through a simple and inexpensive process, and foldable back plate films that do not cause problems such as evaporation of adhesives when cut and stored.

BRIEF SUMMARY OF THE INVENTION

The present application provides a foldable back plate film and a method of manufacturing the same.

One embodiment of the present application provides a foldable back plate film comprising: a foldable back plate comprising a polyimide (PI) substrate, a first adhesive layer provided on one surface of the polyimide substrate, and a second adhesive layer provided on an opposite surface of the surface of the polyimide substrate in contact with the first adhesive layer; a first release film provided on an opposite surface of the surface of the first adhesive layer in contact with the polyimide substrate; and a second release film provided on an opposite surface of a surface of the second adhesive layer in contact with the polyimide substrate, wherein at least one width of the foldable back plate is smaller than the width of each of the first release film and the second release film.

Another embodiment of the present application provides a method of manufacturing a foldable back plate film comprising: preparing a polyimide (PI) substrate; coating a first adhesive layer on one surface of the polyimide substrate; laminating a first release film on an opposite surface of the surface of the first adhesive layer in contact with the polyimide substrate; preparing a second release film; coating a second adhesive layer on one surface of the second release film; laminating an opposite surface of the surface of the second adhesive layer in contact with the second release film on an opposite surface of the surface of the polyimide substrate provided with the first adhesive layer; peeling the first release film from the first adhesive layer; half-blanking and scraping the first adhesive layer, the polyimide substrate and the second adhesive layer; and adhering the first release film onto the first adhesive layer.

Advantageous Effects

The foldable back plate film according to one embodiment of the present application comprises a first adhesive layer and a second adhesive layer on both surfaces of a back plate substrate so that the back plate can be adhered to the display panel of the flexible substrate and a support can be attached to an opposite surface thereof without an additional process of forming a tackifier or an adhesive agent.

In addition, in the foldable back plate film according to the present application, at least one width of the foldable back plate is formed to be smaller than the width of the first release film and the width of the second release film, thus preventing problems of contamination of the cross-section and evaporation even when the first adhesive layer and the second adhesive layer are cut and stored.

In addition, the manufacturing method of the foldable back plate film according to the present disclosure enables the number of processing steps to be reduced by directly coating the first adhesive layer on the back plate substrate and then laminating the first release film thereon, reduces the amount of film that is used, and increases adhesiveness with the back plate substrate owing to the direct coating.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a sectional view showing the laminated structure of a foldable back plate film according to one embodiment of the present application.

FIG. 2 is an optical microscope (OM) image of the foldable back plate film according to Example 1 of the present application.

FIG. 3 is an optical microscope (OM) image of the foldable back plate film according to Comparative Example 1 of the present application.

FIG. 4 is an optical microscope (OM) image of the foldable back plate film according to Comparative Example 1 of the present application.

FIG. 5 is an optical microscope (OM) image of the foldable back plate film according to Comparative Example 1 of the present application.

REFERENCE NUMERAL

-   -   101: First release film     -   102: First adhesive layer     -   103: Polyimide substrate     -   104: Second adhesive layer     -   105: Second release film     -   106: Foldable back plate

DETAILED DESCRIPTION OF THE INVENTION

Hereinafter, the present application will be described in more detail.

In the present application, it will be understood that, when a portion is referred to as “including” one element, the portion may further comprise another element, and does not preclude the presence thereof unless clearly indicated otherwise.

Hereinafter, specific embodiments of the present invention will be described in more detail with reference to the attached drawings such that those skilled in the art to which the present invention pertains can easily implement the embodiments. However, the present invention can be implemented in various forms and is not limited to the embodiments described herein.

One embodiment of the present application provides a foldable back plate film comprising: a foldable back plate comprising a polyimide (PI) substrate, a first adhesive layer provided on one surface of the polyimide substrate, and a second adhesive layer provided on an opposite surface of a surface of the polyimide substrate in contact with the first adhesive layer; a first release film provided on an opposite surface of a surface of the first adhesive layer in contact with the polyimide substrate; and a second release film provided on an opposite surface of the surface of the second adhesive layer in contact with the polyimide substrate, wherein at least one width of the foldable back plate is smaller than a width of each of the first release film and the second release film.

The foldable back plate film according to one embodiment of the present application comprises the first adhesive layer and the second adhesive layer on both surfaces of the back plate substrate so that the back plate can be adhered onto the display panel of the flexible substrate and a support can be attached to an opposite surface thereof, without an additional process of forming a tackifier or an adhesive agent.

In addition, in the foldable back plate film according to the present application, at least one width of the foldable back plate is formed to be smaller than the width of the first release film and the width of the second release film, thus preventing problems of contamination of the cross-section and evaporation even when the first adhesive layer and the second adhesive layer are cut and stored.

FIG. 1 shows a laminated structure of a foldable back plate film according to the present application, and specifically shows that a first adhesive layer 102 and a second adhesive layer 104 are provided on both surfaces of a polyimide (PI) substrate 103, a first release film 101 is provided on one surface of the first adhesive layer 102 and a second release film 105 is provided on one surface of the second adhesive layer 104, and the width of a foldable back plate 106 is smaller than the width of the first release film 101 and the width of the second release film 105.

The width of each of the foldable back plate, the first release film and the second release film means a length in a direction perpendicular to the lamination direction of the foldable back plate film, which can be seen in FIG. 1. More specifically, the width 108 of the foldable back plate and the width 107 of the first and second release films can be seen and are disposed in a direction perpendicular to the lamination direction of the foldable back plate film.

In the case of the foldable back plate film according to the present application, at least one width of the foldable back plate is formed to be smaller than the width of each of the first release film and the second release film, thus preventing foreign matter such as dust from easily attaching to the cut surfaces of the first and second adhesive layers, making it easy to subsequently remove the first release film and the second release film, and preventing damage to the first adhesive layer and the second adhesive layer.

In the foldable back plate film according to one embodiment of the present application, the storage modulus (G1) of the polyimide substrate at 20° C. satisfies the following Equation 1, the peel force at 23° C. of the second release film from the second adhesive layer is 20 gf/inch or less, and the peel force of the first release film from the first adhesive layer is lower than the peel force of the second release film from the second adhesive layer.

1 GPa≤G1≤5 GPa   [Equation 1]

In one embodiment of the present application, G1 satisfies 1 GPa≤G1≤5 GPa, preferably 1.5 GPa≤G1≤4 GPa, and more preferably 2 GPa≤G1≤4 GPa.

The polyimide substrate according to the present application satisfies the range of G1, thus maintaining reliability even after repeated folding multiple times, minimizing stress values generated during folding and realizing sufficient hardness to support the display panel when subsequently applied to the back plate of the foldable display.

One embodiment of the present application provides a foldable back plate wherein an elongation at break at 20° C. of the polyimide substrate is 20% or more and 200% or less.

In another embodiment, the elongation at break of the polyimide substrate at 20° C. is 20% or more and 200% or less, preferably 40% or more and 180% or less, more preferably 70% or more and 150% or less.

The elongation at break of the polyimide substrate means (L2−L1)/L1*100(%) wherein L1 represents the initial length of the polyimide substrate and L2 represents the length of a fracture occurring when stretched.

The storage modulus (G1) and the elongation at break were measured in accordance with the method of KS M ISO527 using a UTM produced by Zwick Corporation. The film to be measured is cut to pieces 5 mm in width and 60 mm or longer in length, the distance between the grips is set to 40 mm, and the storage modulus (G1) and the elongation at break can be determined by values measured while pulling the sample film at a rate of 20 mm/min.

One embodiment of the present application provides a foldable back plate film wherein the polyimide substrate has a heat shrinkage at 200° C. of 0.1% or less.

In another embodiment, the heat shrinkage at 200° C. of the polyimide substrate may be 0.1% or less, preferably 0.09% or less, and more preferably 0.08% or less.

In another embodiment, the heat shrinkage at 200° C. of the polyimide substrate may be 0.03% or more.

“Heat shrinkage” refers to the degree of shrinkage in the direction having a maximum shrinkage force when heat is applied to the polyimide substrate, and means (M1−M2)/M1*100, wherein M1 represents the initial length of the polyimide substrate and M2 represents the shrinkage length in the shrinkage direction after heating at 200° C. for 2 hours.

As the polyimide substrate has the heat shrinkage force in the above range, even when heat is applied in the back-plate coating process, the shrinkage force is low and thus deformation does not occur.

The foldable back plate according to the present application uses the polyimide substrate satisfying the above conditions, thereby avoiding plastic deformation of the back plate and providing excellent durability even when the folding and unfolding operations of the foldable display is repeated, and restoring the strain generated during folding without permanent deformation during unfolding.

One embodiment of the present application provides a foldable back plate film wherein the storage modulus at −30° C. of the first adhesive layer and the second adhesive layer is G2, the storage modulus at 60° C. of the first adhesive layer and the second adhesive layer is G3, and G2 and G3 satisfy the following Equations 2 and 3 below.

1×10⁴ Pa≤G2≤1×10⁶ Pa   [Equation 2]

1×10⁴ Pa≤G3≤1×10⁶ Pa   [Equation 3]

In one embodiment of the present application, G2 satisfies 1×10⁴ Pa≤G2≤1×10⁶ Pa, preferably 1×10⁵ Pa≤G2≤1×10⁶ Pa, and more preferably 1×10⁵ Pa≤G2≤9×10⁵ Pa.

In one embodiment of the present application, G3 satisfies 1×10⁴ Pa≤G3≤1×10⁶ Pa, preferably 1×10⁴ Pa≤G3≤1×10⁵ Pa, and more preferably 1×10⁴ Pa≤G3≤8×10⁴ Pa.

G2 and G3 satisfy the predetermined ranges, thereby minimizing stress during folding and preventing generation of foreign matter or bleeding out during the cutting process or storage process.

In one embodiment of the present application, the storage modulus is measured by laminating the adhesive layer multiple times, cutting the same into a specimen having a thickness of 1 mm and measuring a parallel plate fixture having a diameter of 8 mm using an advanced Rheometric Expansion System G2 (TA Corp) under the conditions of 1 Hz, 5% strain and 10° C./min.

One embodiment of the present application provides a foldable back plate film wherein an initial adhesive force (gf/inch) of each surface of the first adhesive layer and the second adhesive layer in contact with the polyimide substrate after standing at 23° C./humidity 50% for 2 hours is A1, the late adhesive force (gf/inch) of each surface after standing at 60° C./humidity 90% for 20 days is A2, and A1 and A2 satisfy the following Equation 4:

A1×0.8≤A2   [Equation 4]

In one embodiment of the present application, A1 is 500 gf/inch or more and 2,000 gf/inch or less, preferably 600 gf/inch or more and 1,800 gf/inch or less, and more preferably 800 gf/inch or more and 1,500 gf/inch or less.

In one embodiment of the present application, A2 is 400 gf/inch or more and 2,500 gf/inch or less, preferably 500 gf/inch or more and 2,000 gf/inch or less, and more preferably 650 gf/inch or more and 1,800 gf/inch or less.

A1 and A2 of the first adhesive layer and the second adhesive layer satisfy the predetermined ranges, thereby maintaining the adhesive force to the back plate substrate even under high-temperature high-humidity conditions, thus avoiding lifting and bubbling.

In one embodiment of the present application, the first adhesive layer and the second adhesive layer may comprise at least one selected from the group consisting of an acrylic adhesive layer, a rubber adhesive layer and a silicone adhesive layer.

In another embodiment, the first adhesive layer and the second adhesive layer may comprise an acrylic adhesive layer.

One embodiment of the present application provides a foldable back plate film wherein the peel force at 23° C. of the first release film from the first adhesive layer is 12 gf/inch or less.

In another embodiment, the peel force at 23° C. of the first release film from the first adhesive layer may be 12 gf/inch or less, preferably 11 gf/inch or less, and more preferably 10 gf/inch or less.

In another embodiment, the peel force at 23° C. of the first release film from the first adhesive layer may be 3 gf/inch or more, preferably 4 gf/inch or more, and more preferably 5 gf/inch or more.

In one embodiment of the present application, the peel force at 23° C. of the second release film from the second adhesive layer is 20 gf/inch or less.

In another embodiment, the peel force at 23° C. of the second release film from the second adhesive layer may be 20 gf/inch or less, preferably 19 gf/inch or less, and more preferably 18 gf/inch or less.

In another embodiment, the peel force at 23° C. of the second release film from the second adhesive layer may be 10 gf/inch or more, preferably 11 gf/inch or more, and more preferably 12 gf/inch or more.

The peel force of the first release film from the first adhesive layer and the peel force of the second release film from the second adhesive layer were measured at an angle of 180° and a peeling speed of 2,400 mm/min using a texture analyzer (Stable Micro Systems Co., Ltd.) and the peel force of the foldable back plate film prepared according to the present disclosure was measured at 23° C.

The foldable back plate film according to the present application comprises the first release film and the second release film on the first adhesive layer and the second adhesive layer, respectively, and the peel force of the first release film from the first adhesive layer is controlled to be lower than the peel force of the second release film from the second adhesive layer, thus preventing the second release film from being lifted, even when the first release film is removed, during adhesion of the back plate substrate to the display panel of the flexible substrate, and the peel force of the second release film from the second adhesive layer has the predetermined range, thereby preventing the display panel from being damaged even when the second release film is removed to attach the support to the back plate substrate.

That is, the foldable back plate film according to the present application has adhesive layers on both surfaces of the back plate substrate, thereby requiring no additional process when bonding to the display panel and the support, and the peel force of the release film from each adhesive layer is medium or weak, thereby preventing damage to the display panel and the back plate substrate when the back plate is bonded thereto.

One embodiment of the present application provides a foldable back plate film wherein the surface resistance of the first release film and the second release film is 10¹⁰ n/sq or less at 500V or less.

One embodiment of the present application provides a foldable back plate film wherein the surface resistance at 500V or less of the first release film and the second release film is 10¹⁰ n/sq or less, preferably, 3×10⁹ n/sq or less and more preferably 1×10⁹ n/sq or less.

In another embodiment of the present application, the surface resistance of the first release film and the second release film is 10⁷ n/sq or more at 500V or less.

The surface resistance of the first release film and the second release film can be measured using a concentric electrode on the back surface of the test specimen PET, and can be measured at an applied voltage of 500V, and at 25° C. and 55 RH % for an applied time of 10 seconds using MCT-HT800 (Mitsubishi Co., Ltd.).

The first release film and the second release film have surface resistance values within the range defined above due to antistatic treatment, thereby preventing subsequent damage to the display panel due to static electricity when the first release film is peeled off and the first release film and the second release film are then attached to the bottom of the display panel.

The first and second release films refer to transparent layers attached to one surface of the first and second adhesive layers in order to protect the first and second adhesive layers, which are very thin, and may be films having excellent mechanical strength, thermal stability, moisture-blocking property, isotropy and like. For example, the first and second release films may be acetate (such as triacetyl cellulose, TAC), polyester, polyether sulfone, polycarbonate, polyamide, polyimide, polyolefin, cycloolefin, polyurethane, silicone or acrylic resin films or the like. Any commercially available silicone release film may be used without limitation.

In one embodiment of the present application, the first release film and the second release film may be further subjected to an anti-static treatment to prevent damage to the display panel by static electricity when attached to the bottom of the display panel.

One embodiment of the present application provides a foldable back plate film, wherein the polyimide substrate has a thickness of 20 μm or more and 120 μm or less.

In another embodiment, the polyimide substrate may have a thickness of 20 μm or more and 120 μm or less, preferably 30 μm or more and 100 μm or less, and more preferably 40 μm or more and 80 μm or less.

Since the polyimide substrate has a thickness within the predetermined range, the polyimide substrate can efficiently serve as a support when the polyimide substrate is used as a back plate of a foldable display, does not cause handling problems during roll coating, and has a suitable radius-of-curvature deviation and thus minimizes stress when folding.

One embodiment of the present application provides a foldable back plate film wherein each of the first adhesive layer and the second adhesive layer has a thickness of 10 μm or more and 100 μm or less.

In another embodiment, each of the first adhesive layer and the second adhesive layer has a thickness of 10 μm or more and 100 μm or less, preferably 15 μm or more and 80 μm or less, and more preferably 15 μm or more and 50 μm or less.

When the first adhesive layer and the second adhesive layer are within the predetermined thickness ranges, stress is minimized during folding, thereby minimizing deformation as compared to thickness. When the first adhesive layer and the second adhesive layer are within the predetermined thickness ranges, radius-of-curvature deviation is suitable, thus minimizing stress applied to the outermost film when folding.

One embodiment of the present application provides a foldable back plate film, wherein the thickness of each of the first release film and the second release film is 10 μm or more and 150 μm or less.

In another embodiment, each of the first release film and the second release film has a thickness of 10 μm or more and 150 μm or less, preferably 15 μm or more and 125 μm or less, and more preferably 25 μm or more and 50 μm or less.

Since the thickness of each of the first release film and the second release film is within the predetermined range, there is an advantage in that handling during roll coating is excellent.

One embodiment of the present application provides a foldable back plate film wherein at least one width of the foldable back plate is R1, the width of each of the first release film and the second release film is R2, and R1 and R2 satisfy the following Equation 5:

1 mm≤R2−R1≤20 mm   [Equation 5]

In one embodiment of the present application, Equation 5 may be 1 mm≤R2−R1≤20 mm, preferably 2 mm≤R2−R1≤15 mm, and more preferably 3 mm≤R2−R1≤10 mm.

The foldable back plate film according to the present application satisfies Equation 5 above, thereby preventing foreign matter such as dust from being easily attached to the cut surfaces of the first and second adhesive layers, making it easy to subsequently remove the first release film and the second release film, thus preventing damage to the first adhesive layer and the second adhesive layer, and preventing problems of contamination of the cross-section and evaporation even when the first adhesive layer and the second adhesive layer are cut and stored.

In one embodiment of the present application, R1 may satisfy 100 mm≤R1≤500 mm, preferably 150 mm≤R1≤450 mm, and more preferably 200 mm≤R1≤400 mm.

In one embodiment of the present application, R2 may satisfy 120 mm≤R2≤600 mm, preferably 250 mm≤R2≤550 mm, and more preferably 300 mm≤R2≤500 mm.

In one embodiment of the present application, the width of the first release film and the width of the second release film may be identical to each other.

In one embodiment of the present application, the width of the first release film and the width of the second release film may be different from each other.

In one embodiment of the present application, in the case where the widths of the first release film and the second release film are different, R2 indicates the smaller one among the width of the first release film and the width of the second release film.

Another embodiment of the present application provides a method of manufacturing a foldable back plate film comprising: preparing a polyimide (PI) substrate; coating a first adhesive layer on one surface of the polyimide substrate; laminating a first release film on an opposite surface of the surface of the first adhesive layer in contact with the polyimide substrate; preparing a second release film; coating a second adhesive layer on one surface of the second release film; laminating an opposite surface of the surface of the second adhesive layer in contact with the second release film on an opposite surface of the surface of the polyimide substrate provided with the first adhesive layer; peeling the first release film from the first adhesive layer; half-blanking and scraping the first adhesive layer, the polyimide substrate and the second adhesive layer; and adhering the first release film onto the first adhesive layer.

The description of each layer included in the foldable back plate film is the same as mentioned above.

The manufacturing method of the foldable back plate film according to the present disclosure enables the number of processing steps to be reduced by directly coating the first adhesive layer on the back plate substrate and then laminating the first release film thereon, reduces the amount of film that is used, and increases adhesiveness with the back plate substrate owing to the direct coating.

When manufacturing the foldable back plate film in accordance with the method described above, like the foldable back plate film according to the present application, a foldable back plate film wherein at least one width of the foldable back plate is smaller than the width of each of the first release film and the second release film can be obtained.

One embodiment of the present application provides a method of manufacturing a foldable back plate film wherein the coating a first adhesive layer and the coating a second adhesive layer are carried out by direct coating.

The method of manufacturing a foldable back plate film according to the present disclosure is carried out by direct coating, thereby making it to easily change the release force of the first release film and the second release film. The foldable back plate film thus manufactured is characterized in that the peel force of the first release film from the first adhesive layer may be lower than the peel force of the second release film from the second adhesive layer.

In one embodiment of the present application, in the steps of peeling the first release film from the first adhesive layer and half-blanking and scraping the first adhesive layer, the polyimide substrate and the second adhesive layer, the peel force of the first release film from the first adhesive layer is lower than the peel force of the second release film from the second adhesive layer, thereby preventing damage to the foldable back plate film in the manufacturing process and increasing ease of processing.

In the foldable back plate film according to the present application, after removing the first release film and the second release film, one surface thereof may be attached to the display panel of the foldable display, and the other surface thereof may be attached to a support of the back plate.

The support may serve as a guide for folding the foldable display, any foldable support may be used without limitation, and commercially available materials such as plastics, metals and highly rigid films may be used as necessary without limitation.

Hereinafter, specific examples of the present invention will be described in more detail such that those skilled in the art to which the present invention pertains can easily implement the examples. However, the present invention can be implemented in various forms and is not limited to the examples described herein.

Production Example

<Production of Foldable Back Plate Film>

1. Preparation of First Copolymer

A monomer mixture of ethylhexyl acrylate (EHA) and acrylic acid (AA) was added to a 1L reactor, in which nitrogen gas was refluxed and in which a cooler was installed to facilitate temperature control, and then ethyl acetate (EAc) was added as a solvent thereto. Then, nitrogen gas was purged for about 1 hour to remove oxygen and then the reactor temperature was maintained at 62° C. The mixture was homogeneously mixed, 400 ppm of azobisisobutyronitrile (AIBN) as a reaction initiator and 400 ppm of n-dodecylmercaptan (n-DDM) as a chain transfer agent were added thereto, and the resulting mixture was allowed to react. After the reaction, EAc was diluted to prepare a copolymer having a weight average molecular weight of 2 million.

2. Production of Adhesive Layer-1

An epoxy-based crosslinking agent was added to 100 g of the first copolymer prepared as described above, and was diluted to 18% by weight in an ethyl acetate solution and then mixed homogenously. The adhesive composition polymerized in accordance with the designed composition was diluted in a solvent for adjusting a solid content to provide a viscosity suitable for coating (500 to 1,500 cp) and was then mixed for 15 minutes or more using a mechanical stirrer. The mixture was allowed to stand at room temperature to remove the bubbles generated during mixing, and a coating film was formed using an applicator and then dried at 140° C. for 3 minutes using a Mathis oven to prepare an adhesive layer-1.

3. Production of Foldable Back Plate Film

1) Examples 1 to 3

The adhesive layer-1 prepared above was coated on one surface of a back plate substrate having the physical properties shown in Table 1 below, and a light-peeling release film of Table 1 was laminated on an opposite side of a surface of the adhesive layer-1 in contact with the back plate substrate.

Then, the heavy-peeling release film shown in Table 1 was prepared, the adhesive layer-1 prepared above was coated on the heavy-peeling release film, and the opposite surface of the surface of the adhesive layer-1 in contact with the heavy-peeling release film and the opposite side of the surface on which the adhesive layer-1 of the back plate substrate prepared above was formed were laminated to produce a foldable back plate film having a triple-layer structure (adhesive layer/back plate/adhesive layer).

Then, the light-peeling release film was peeled from the adhesive layer-1, and then the adhesive layer-1, the back plate and the adhesive layer-1 were half-blanked and scraped under the conditions of the following Table 2, and then the light-peeling release film was re-attached to the adhesive layer-1 to produce a foldable back plate film having a sandwich structure.

2) Comparative Example 1

A foldable back plate film was produced in the same manner as in Example 1, except that the half-blanking and scraping processes were not performed.

TABLE 1 Configuration of foldable 3 layers back plate 25/50/25 μm Adhesive Storage modulus (G′, Pa) @−30° C. 5.4 × 10{circumflex over ( )}5 Storage modulus (G′, Pa) @60° C.   3 × 10{circumflex over ( )}4 Tensile Stress Relaxation Initial Stress 12941 (DMA) Temperature: −20° C. Strain: 12% Final Stress 6682 Time: deformation for Stress drop (%) 48.4 10 min PI adhesive force (gf/in, Initial 1167 2.4 mpm) 80° C. 20 days 1316 60° C. 20 days 1326 Back plate Storage modulus (E′, GPa) @20° C. 2.6 substrate Elongation at break (%) @20° C. 116 Heat shrinkage (%) 200°, 2 hr, 0.04 IPC-TM-650 2.2.4 Method A Release Light-peeling release peel force 7 film (gf/in, 2.4 mpm) Medium-peeling release peel force 14 (gf/in, 2.4 mpm) Static folding (60° C. 90% RH, 2.5 R, 20 days) OK Dynamic folding (25° C., 2.5 R, 100,000 times) OK Waviness after folding test OK

TABLE 2 Ex. 1 Ex. 2 Ex. 3 Comp. Ex. 1 R2-R1 (mm) 6 8 9 0

In Table 2, one width of the back plate substrate is R1, and the width of each of the light-peeling release film and the heavy-peeling release film is R2.

FIG. 2 shows an optical microscope (OM) image of the foldable back plate film of Example 1, and FIGS. 3 to 5 show an optical microscope (OM) image of Comparative Example 1.

As can be seen from FIGS. 2 to 5, the foldable back plate film according to the present application has a sandwich structure in which at least one width of the foldable back plate is smaller than the width of each of the first release film and the second release film, thereby preventing foreign matter such as dust from being easily attached to the cut surfaces of the first and second adhesive layers, making it easy to subsequently remove the first release film and the second release film, preventing damage to the first adhesive layer and the second adhesive layer upon removal of the release films, and preventing problems of contamination of the cross-section and evaporation even when the first adhesive layer and the second adhesive layer are cut and stored.

Specifically, it can be seen from FIG. 3 that evaporation occurs, it can be seen from FIG. 4 that bubbles are generated, and it can be seen from FIG. 5 that the adhesive layer is torn upon removal of the first and second release films. 

1. A foldable back plate film comprising: a foldable back plate comprising a polyimide (PI) substrate, a first adhesive layer provided on an surface of the polyimide substrate, and a second adhesive layer provided on a surface opposite side of the surface of the polyimide substrate in contact with the first adhesive layer; a first release film provided on surface opposite side of the surface of the first adhesive layer in contact with the polyimide substrate; and a second release film provided on surface opposite side of theft surface of the second adhesive layer in contact with the polyimide substrate, wherein at least one width of the foldable back plate is smaller than a width of each of the first release film and the second release film, the width being a length in a direction perpendicular to the lamination direction of the foldable back plate film.
 2. The foldable back plate film of claim 1, wherein a storage modulus (G1) at 20° C. of the polyimide substrate satisfies Equation 1, and wherein a peel force at 23° C. of the second release film from the second adhesive layer is 20 gf/inch or less, and a peel force at 23° C. of the first release film from the first adhesive layer is lower than the peel force of the second release film from the second adhesive layer. 1 GPa≤G1≤5 GPa   [Equation 1]
 3. The foldable back plate film of claim 1, wherein a storage modulus at −30° C. of the first adhesive layer and the second adhesive layer is G2, a storage modulus at 60° C. of the first adhesive layer and the second adhesive layer is G3, and G2 and G3 satisfy Equations 2 and 3 below. 1×10⁴ Pa≤G2≤1×10⁶ Pa   [Equation 2] 1×10⁴ Pa≤G3≤1×10⁶ Pa   [Equation 3]
 4. The foldable back plate film of claim 1, wherein an initial adhesive force (gf/inch) of each surface of the first adhesive layer and the second adhesive layer in contact with the polyimide substrate after standing at 23° C. and humidity 50% for 2 hours is A1, and a late adhesive force (gf/inch) of the each surface after standing at 60° C. and/humidity 90% for 20 days is A2, and A1 and A2 satisfy Equation 4: A1×0.8≤A2   [Equation 4]
 5. The foldable back plate film of claim 1, wherein an elongation at break at 20° C. of the polyimide substrate is 20% or more and 200% or less.
 6. The foldable back plate film of claim 1, wherein a heat shrinkage at 200° C. of the polyimide substrate is 0.1% or less.
 7. The foldable back plate film of claim 1, wherein a peel force at 23° C. of the first release film from the first adhesive layer is 12 gf/inch or less.
 8. The foldable back plate film of claim 1, wherein the polyimide substrate has a thickness of 20 μm or more and 120 μm or less.
 9. The foldable back plate film of claim 1, wherein each of the first adhesive layer and the second adhesive layer has a thickness of 10 μm or more and 100 μm or less.
 10. The foldable back plate film of claim 1, wherein at least one width of the foldable back plate is R1, the width of each of the first release film and the second release film is R2, and R1 and R2 satisfy Equation 5: 1 mm≤R2−R1≤20 mm   [Equation 5]
 11. The foldable back plate film of claim 1, wherein the first release film and the second release film are each a silicone-based films.
 12. The foldable back plate film of claim 1, wherein each of the first release film and the second release film has a surface resistance of 10¹⁰ Ω/sq or less at 500V or less.
 13. A method of manufacturing a foldable back plate film comprising: providing a polyimide (PI) substrate; coating a first adhesive layer on a surface of the polyimide substrate; laminating a first release film on a surface opposite side of the surface of the first adhesive layer in contact with the polyimide substrate; providing a second release film; coating a second adhesive layer on a surface of the second release film; laminating a surface opposite side of the surface of the second adhesive layer in contact with the second release film on a surface opposite side of the surface of the polyimide substrate provided with the first adhesive layer; peeling the first release film from the first adhesive layer; half-blanking and scraping the first adhesive layer, the polyimide substrate and the second adhesive layer; and adhering the first release film onto the first adhesive layer.
 14. The method of claim 13, wherein the coating the first adhesive layer and the coating the second adhesive layer are carried out by direct coating. 